Kianinia Y, Darban A K, Taheri-Nassaj E, Rahnama B, Foroutan A. SYNTHESIS OF NANO SIZED MESOPOROUS γ - Al2O3POWDER FROM DOMESTIC HAMEDAN KAOLIN. IJMSE 2015; 12 (1) :59-65
URL: http://ijmse.iust.ac.ir/article-1-768-en.html
Abstract:   (18055 Views)
A method for producing high surface area nano-sized mesoporous alumina from inexpensive Iranian kaolin as raw material is proposed. In this method, first, kaolin was purified for purifying Kaolin, High Grade Magnetic Separation and leaching with HCl and chemical bleaching treatment by using sodium dithionite (Na 2 S 2O4 ) as reducing agent in acidic media (H 2SO 4 ) were used. Purified kaolin was calcined. After that, Al (hydr) oxide from acid -leachates of calcined kaolin was precipitated with ammonia, in presence of polyethylene glycol. Finally, a white powder of nano-sized alumina particles was obtained after calcination. BET surface area, X-ray diffraction (XRD), Fourier transform infrared spectroscopy (FT-IR) and scanning electron microscopy (SEM) were used to characterize the sample. The resulting alumina with relatively high surface area (201.53 m 2 g -1 ) and narrow mean pore diameter (6.91 nm), consists of a particle size distribution ranging from 22 to 36 nm.
Full-Text [PDF 6036 kb]   (4839 Downloads)    
Type of Study: Research Paper | Subject: Ceramics

Add your comments about this article : Your username or Email:
CAPTCHA

Send email to the article author


Rights and permissions
Creative Commons License This work is licensed under a Creative Commons Attribution-NonCommercial 4.0 International License.

© 2022 All Rights Reserved | Iranian Journal of Materials Science and Engineering

Designed & Developed by : Yektaweb