H. Momeni, H. Razavi, S. G. Shabestari,
Volume 8, Issue 2 (6-2011)
Abstract
Abstract: The supersolidus liquid phase sintering characteristics of commercial 2024 pre-alloyed powder was studied at different sintering conditions. Pre-alloyed 2024 aluminum alloy powder was produced via air atomizing process with particle size of less than 100 µm. The solidus and liquidus temperatures of the produced alloy were determined using differential thermal analysis (DTA). The sintering process was performed at various temperatures ranging from the solidus to liquidus temperatures in dry N2 gas atmosphere for 30 min in a tube furnace. The maximum density of the 2024 aluminum alloy was obtained at 610ºC which yields parts with a relative density of 98.8% of the theoretical density. The density of the sintered samples increased to the maximum 99.3% of the theoretical density with the addition of 0.1 wt. %Sn powder to the 2024 pre-alloyed powder. The maximum density was obtained at 15% liquid volume fraction for both powder mixtures.
Mala Siddaramappa, Haraluru Kamala Eshwaraiah Latha, Haraluru Shankaraiah Lalithamba, Andi Udayakumar,
Volume 18, Issue 4 (12-2021)
Abstract
Indium tin oxide (ITO) nanoparticles were synthesized by green combustion method using indium (In) and tin (Sn) as precursors, and Carica papaya seed extract as novel fuel. This paper highlights effect of tin concentration (5%, 10% and 50%) on microstructural, optical and electrical properties of ITO nanoparticles (NPs). The indium nitrate and tin nitrate solution along with the fuel were heated at 600 °C for 1 h in muffle furnace and obtained powder was calcinated at 650 °C for 3 h to produce ITO NPs. The above properties were investigated using XRD, FTIR, UV-Vis spectroscopy, SEM, TEM and computer controlled impedance analyser. The XRD, SEM and TEM investigations reveals the synthesized NPs were spherical in shape with an increase in average grain size (17.66 to 35 nm) as Sn concentration increases. FTIR investigations confirms the In-O bonding. The optical properties results revealed that the ITO NPs band gap decreased from 3.21 to 2.98 eV with increase in Sn concentration. The ac conductivity of ITO NPs was found to increase with increase in Sn concentration. These synthesised ITO NPs showed the excellent properties for emerging sensor and optical device application.