Showing 366 results for Co
Paydar M.h., Fadaei R., Shariat M.h.,
Volume 2, Issue 2 (6-2005)
Abstract
Copper coated SiC powders having three different amounts of copper, in the range of 20-60 wt%, were prepared via electroless coating process. The produced composite powders were uniaxially cold compressed and sintered at different temperatures and times under protective atmosphere. It was found that composite Cu/SiC powders and a relatively dense copper matrix composite with a uniform distribution of SiC reinforcing particles imbedded in copper matrix can be fabricated via electroless coating method followed by conventional cold pressing and sintering process. The results also show that SiC particles have a poor wettability with copper and so liquid phase sintering of the Cu/SiC composite powders did not enhance densification of the samples. Regarding this fact, optimum sintering temperatures, which depends on copper content, was determined to be in the range of 1050-1080?C.
Morakabati M., Arabi H., Mirdamadi Sh., Abbasi S.m.,
Volume 2, Issue 2 (6-2005)
Abstract
This study was launched to investigate the effects of heating rate and aging parameters on the kinetic of precipitation reactions in a high alloy high strength steel having Ni, Co, Mo and Ti. For this purpose, as quenched specimens were subjected to three types of aging methods with different heating rates. These methods consisted of aging in Pb bath, salt bath, and furnace at different aging cycles. The kinetic of precipitation in each method was studied by hardness measurements and was described adequately by the Johnson-mehl-Avrami equation. Remarkable increase in hardness and its rate is observed when the rate of heating increases. The substantial increase in hardness of the specimens aged rapidly in salt & Pb baths, compared with those aged normally in furnace, seemed to be due to the formation of thermo elastic stresses during sudden expansion of the substance subjected to rapid heating. According to the results obtained in this research, increase in the Avrami constants, n & k, and decrease in the start time of transformation, ts, are associated with heating rate increasing. Analysis of the observed and calculated data for hardness using Arrhenius equation, shows that for the same amount of volume fraction of precipitates, the activation energy of precipitates decreased for f=25 and 50%, while at f=90 % it increased by increasing heating rate.
Ghobeiti Hasab M., Seyyed Ebrahimi S.a., Badaee A.,
Volume 2, Issue 2 (6-2005)
Abstract
In this research the sol-gel auto-combustion method was used to prepare strontium hexaferrite nanopowder. A solution of distilled water, ferric and strontium nitrates, citric acid, trimethylamine, and n-decyltrimethylammonium bromide cationic surfactant, was heated to form a viscous gel. The gel was heated and then ignited automatically. As-burnt powder was calcined at temperatures from 700 to 900?C in air to obtain SrO.6Fe2O3 phase. The influence of the calcination temperature on the phase composition of the products has been investigated. X-ray diffraction confirmed the formation of single-phase strontium hexaferrite nanopowder at temperature of 800?C.
Razaghian A., Yu D., Chandra T.,
Volume 2, Issue 3 (9-2005)
Abstract
Fracture behavior of a 7075 aluminium alloy reinforced with 15 Vol%. SiC particles was studied after T6 and annealing heat treatments under uniaxial tensile loading at room temperature. The scanning electron microscopy of fractured surfaces and EDS analysis showed:, that fracture mechanism changed from due mainly to fractured particle in T6 condition to interface decohesion in samples in annealed state. Different fracture mechanisms in annealed and T6 conditions can be ascribed mainly to the significant difference in the stress concentration levels around the particles. In T6 condition, very high local stress sufficient to cause fracture of particle can be generated during loading, while the presence of large precipitates at the particle/matrix interface produced interface decohesion leading to final fracture in the annealed state.
Mirbagheri S.m.h., Chirazi A.,
Volume 2, Issue 3 (9-2005)
Abstract
A numerical model has been developed for the determination of liquid flow permeability through columnar dendrite during growth. The model is inclusive two stages, first numerical evolution of the dendrite shape during growth, and second numerical determination of the interdendritic liquid permeability. Simulation results shown which solute concentration by evolution of dendrite shape could result to reduction of the permeability during solidification time. Comparison between the experimental data from other authors and the present numerical model data, for the low and high solid fractions, has shown a good agreement rather than current numerical models. Therefore present permeability model, in this investigation, could be used for all of the micro solidification codes by coupling on the segregation and the Fick's equations in domain of the inter-dendritic liquid for mushy alloys.
Sedghi A., Shokouh Far A., Eslami Farsani R.,
Volume 2, Issue 3 (9-2005)
Abstract
Carbon fibers are fabricated from different materials such as special polyacrylonitrile (PAN) fibers, cellulose fibers and pitch. But PAN fibers are recognized as the most widely used precursor for the present-day manufacture of carbon fibers. The process of fabrication carbon fibers from special PAN fibers is composed of two steps including oxidative stabilization at low temperature and carbonization at high temperatures in an inert atmosphere. Today carbon fibers are still expensive because of the high price of their raw material (special PAN fibers).This study focuses on making carbon fibers from commercial PAN fibers (low price PAN fibers used in textile industry). The results shows that in case of conducting complete stabilization process, it is possible to produce desirable carbon fibers from commercial PAN fibers. With some changes in conventional procedure of stabilization in terms of temperature and time of operation, the desirable conditions of complete stabilization are achieved.
Moayed M.h.,
Volume 2, Issue 3 (9-2005)
Abstract
In this research pitting Corrosion of a sensitized 316 stainless steel was investigated employing potentiodynamic, potentiostatic techniques. Sensitization process was carried out on as-received alloy by submitting the specimen in electric furnace set at 650°Cfor five hours and then the specimen was quenched 25°C water. Potentiodynamic polarization of as received and sensitized specimens in 1M H2SO4 solution at room temperature and 70°C clearly revealed that the sensitization process has caused a magnificent change on electrochemical behavior of the specimen by changing critical current density for passivation, passivation potential and passive current density. Optical microscopy examination of the specimen surface after oxalic acid electrochemical etching also showed the deterioration of grain boundary of sensitized specimen due to chromium carbide precipitation in compared to as-received one. Several anodic potentiodynamic polarization on rode shaped working electrodes prepared from as-received and sensitized specimen in 3.5% NaCl test solution proved an average ~220 mV drop in pitting potential due to sensitization. Anodic potentiostatic polarization at 400 and 200 mV above corrosion potential also demonstrate the deterioration of pitting resistance of alloy as a result of sensitization. Scanning electron microscopy examination of anodically polarized of sensitized specimen at 700mVprior and after oxalic acid etching revealed large stable pits with lacy cover and also openpits with deep crevice for etched specimens.
Moore R.e., Karakus M.,
Volume 2, Issue 4 (12-2005)
Abstract
In situ refractories are defined as brick or unshaped products, which react internally or with furnace atmospheres and/or slag components so as to be enhanced in their performance. Examples of such products are discussed with emphasis on those that are currently employed and are being developed for the melting of iron and steel. Some strategies for the development of future in situ products are outlined.
Homayonifar P., Saboohi Y., Firouz Abadi B.,
Volume 2, Issue 4 (12-2005)
Abstract
Iron and steel is an energy intensive industry and its contribution to the pollution of environment is considerable. Direct reduction iron (DRI) is a major element of an iron and steel production plant. Its share in natural gas and electricity consumption of total plant is estimated to be 70% and 15% respectively. Reduction gases are produced in natural gas reforming unit and its elements are CO and H2. A major consequence of using this technology is high level of CO2 emission, which pollutes the environment. An alternative to the existing technology is utilization of H2 as reducing agent. A comparison of various hydrogen production processes indicate that thermal decomposition of methane provides an attractive option from economical and technical point of view. Therefore, a system for producing hydrogen, based on thermal decomposition technique, has been designed in the framework of the present paper.
Arabi H., Seyedein S.h., Satari M., Tabatabaie N.,
Volume 2, Issue 4 (12-2005)
Abstract
Life assessment on the base of grain boundary creep cavitation of 1%Cr - 0.5%Mo low alloy steel has been discussed in this paper. Since microstructural degradation is one of the most important mechanisms that affects creep life, it is necessary to assess microstructural damage in order to estimate the life. Microstructural damage within the grain boundaries is a continuous phenomena starting from about the beginning of secondary stage of creep process. In this research, the amounts of damage accumulation in the form of grain boundary cavitations for various creep times up to the ends of secondary creep stage for each creep condition was found by using quantitative metallography technique, i.e. image analyser. Then from the data obtained for grain boundary area cavitated and number of cavities per unit area, which was about linear as a function of time for each of creep conditions, the amount of damage in the tertiary stage was estimated for various times. Then a creep damage parameter was proposed for the creep process. Finally, having this damage parameter (?) and using continuum damage mechanics (CDM), a new version of Rabotnov-Kachanov equation for tertiary creep rate was established.
Saremi M., Nouri Delavar A., Kazemi M.,
Volume 2, Issue 4 (12-2005)
Abstract
An investigation of the electrochemical noise generation during Stress Corrosion Cracking (SCC) of 70-30 Brass in Mattson's solution was conducted. The fluctuations of potential and current were monitored. The relationship between potential and current fluctuations has been evaluated in time domain and the obtained data has been analyzed in the frequency domain using Power Spectral Density (PSD). It is shown that 70-30 Brass has characteristic noise behavior during SCC that is step-by-step change in current and potential up to the final stage of fracture, and this may be used for SCC monitoring.
Salahi E., Ebadzadeh T., Moztar Zadeh F., Solati Hashjin M.,
Volume 2, Issue 4 (12-2005)
Abstract
Compositions of Al2O3+Si, SiO2+Al and Al+Si systems were prepared to study the effect of reaction bonding process on the mullite formation. The composition of each system was adopted according to mullite stoichiometery and sintered in 700-1600°C range. Results showed that the formation of reaction bonded mullite starting from Al2O3+Si mixtures, proceeded in two partially overlapping steps, the oxidation of Si to SiO2, and the reaction of SiO2 and Al2O3 to form mullite. In this system, up to 1400°C, conversion of Si to SiO2 was taken place and cristobalite formed, but mullite formation was not observed. Mullite phase started to form at 1450°C. Results indicated that complete reaction was not occurred up to 1600°C and 2 hours soaking time. XRD patterns of samples in Al+ SiO2 system showed that the reaction through sequences: (a) reduction of SiO2 by Al, (b) formation of a- Al2O3 and SiO2-rderived Si oxidation, and (c) mullite formation. X-ray diffraction patterns of heat-treated Al+Si system showed that reaction between Al and oxygen at 900°C was occurred with the reaction product being a- Al2O3 Oxidation of Si and formation of mullite were not detected in this system. SEM micrographs showed that both Al2O3+Si and SiO2+Al systems have similar microstructures, which consisted of a- Al2O3, mullite and free Si. The microstructures of the samples in Al+Si system consisted of a- Al2O3 free Al and Si with intermetallic Al-Si compound.
Nouroozi S., Vardelle A.,
Volume 2, Issue 4 (12-2005)
Abstract
In wire arc spraying, the atomizing air pressure and applied nozzle system are important factors influencing particles characteristics and coating quality. The aim of this paper is to study how the characteristics of particles such as size, velocity and temperature are influenced by the operating conditions in wire arc spray. For that, three types of wires are tested: solid wire of stainless steel 316L, cored wires 97MXC and 98MXC. Arc spray gun is an Arc Jet 9000 manufactured by TAFA. For each condition, the particles temperature and particles velocity are measured using an imaging CCD camera, Spray Watch (Oseir Ltd). Particles size distributions are determined with a laser grain meter. The morphology and composition of particles were evaluated with SEM, EDX and X-Ray diffraction. Results induce important modifications in the particles size distributions and particles velocity. A small diameter nozzle and high atomizing air pressure resulted in a reduction in particles size distributions and an increase in particles velocity.
Sheikhi Moghaddam K., Ataie A.,
Volume 2, Issue 4 (12-2005)
Abstract
Ultra-fine particles of barium hexaferrite have been synthesized by co-precipitation method using barium nitride and iron chloride precursors with a Fe/Ba molar ratio of 11. Co-precipitation was carried out at 25 and 80°C using NaOH as a precipitant. Effect of coprecipitation and annealing temperatures on the phase composition and morphology of the products have been investigated using XRD and SEM, respectively. XRD results indicated existence of BaFeO3-x as a major phase in co-precipitated samples. Analysis of the XRD results also revealed that barium hexaferrite starts to form at a relatively low temperature of 700°C for sample synthesized at 80°C. SEM micrographs exhibit plate-like hexagonal particles of barium hexaferrite for calcined samples. The SEM results showed that the mean particle size of co-precipitated sample at 25°C is smaller than that of 80°C after calcining.
Hadian A.m., Abu Fanas S.h.,
Volume 2, Issue 4 (12-2005)
Abstract
Enhancing the properties of dental resin composites is of interest to researchers. The objective of the present investigation was to improve the strength and fracture toughness of dental composites via addition of silicon carbide whiskers and substitution of commonly used filler materials with stabilized zirconia ceramic powder. It was also intended to study the effect of powder- to- whisker ratio on mechanical properties of the resultant composites. The flexural strength and fracture toughness of composite samples with different whiskers loadings were measured. It was found that addition of whiskers to the composites enhances the mechanical properties of the composites. The strength and fracture toughness increased by increasing the amount of whiskers. The flexural strength of a composite having 60wt% whisker and 10wt% zirconia powder was about 210 MPa while that of the composite having only 60wt% ceramic powder was about 110 MPa. The microstructural examinations revealed that reinforcing mechanism was whiskers pull-out as well as crack deflection.
Alaee M.s.,
Volume 3, Issue 1 (6-2006)
Abstract
plasma-sprayed silicon layers have been used to produce silicon nitride layers with fibrous microstructure which optimizes fracture toughness and strength. SEM examination of the specimens shows that the surface is covered by fine needles and whiskers of Si3N4.In order to study the oxygen contamination effect as well as other contaminants introduced during spraying and nitridation processes, surface sensitive analysis techniques like AES and XPS have been used to determine concentration of these contaminants.
Hosseini Sh., Arabi H., Tamizifar M., Zeyaei A.a.,
Volume 3, Issue 1 (6-2006)
Abstract
In this research, rotating bending fatigue test at minimum to maximum stress ratio of R=-1 was used for investigating the fatigue behavior of Ti-6Al-4V alloy. Both smooth and notched specimens, with elastic concentration factor, kt, of approximately 3.6 and 4.1 were used for this purpose.In addition, the effect of variation in ultimate tensile strength, UTS, on the fatigue behavior of this alloy was studied. S-N curves were drawn and the value of notch sensitivity was obtained or each case.The results showed that the presence of notch in Ti-6Al-4V alloy has a different amount of sensitivity when the notched specimens were subjected to high cycle fatigue (HCF) and low cycle fatigue (LCF) tests. However, the notch sensitivity of this alloy was shown generally to be much lower than steel alloys with similar UTS values. Thus, considering the high compatibility of this alloy with the body environment and its low sensitivity to notch, one can strongly recommend this alloy for use in biomedical application.
Golazar M.a., Mostaghimi J., Coyle T.w.,
Volume 3, Issue 1 (6-2006)
Abstract
Partially stabilized zirconia (PSZ) has been proven to be an excellent candidate as a thermal barrier coating (TBe) for hot sections in, for instance, heat or internal combustion engines and gas turbine parts. The main functions of these coatings are reducing heat losses, reducing fuel consumption, increasing efficiency, and extending durability and life. One of the main problems involved is wear behavior in the development of such coatings for these applications. Using the air plasma spraying (APS) technique, conventional and nanostructured 8 wt % yttria partially stabilized zirconia (Y-PSZ) coatings were deposited on austenitic stainless steel (AISI304) disc-shaped substrates. The coated substrates were subjected to pin-on-disc wear tests, using 10 mm silicon nitride and zirconia balls as the pin. The coefficient of friction was recorded in real time. The weight loss of coated substrates was measured. Coatings were characterized before and after being subjected to wear testing by various techniques including optical microscopy, scanning electron microscopy (SEM), energy dispersive X-ray spectrometry (EDX) and X-ray diffraction (XRD). Effects of various experimental parameters such as wear distance, test temperature, and counter face material were also investigated. Results obtained revealed that, regardless of experimental conditions applied, the nanostructured zirconia coating shows better wear and tribological properties than that of the conventional one.
Rigaud M., Palco S., Paransky E.,
Volume 3, Issue 1 (6-2006)
Abstract
Wear of various basic refractory materials to substitute to currently used magnesia chrome bricks has been studied, measuring matte and slag penetration and dissolution, through different cup and rotary slag tests. High magnesia with and without impregnation, magnesia graphite, magnesia-alumina spinel with and without impregnation, olivine-magnesia and olivine magnesia- graphite bricks, as well as magnesia-graphite and olivine magnesia castables, have been tested. It has been shown that carbon impregnation and graphite introduction into basic refractories are feasible ways to enhance their corrosion-dissolution and penetration resistance against fayalite as well as calcium-ferrite slags. Olivine-based refractories (castables or bricks) may be considered as viable candidates to use in copper-making furnaces. At this point, evaluation of the thermo-mechanical properties of this new class of materials is still missing.
Arabi H., Divandari M., Hosseini A.h.m.,
Volume 3, Issue 3 (12-2006)
Abstract
In this research the influence of Ti contents on the amounts of inclusions formation and mechanical properties of a high alloy high strength steel, C300, has been investigated. For this purpose several bars were casted under the same solidification conditions, but different amounts of Ti element. All the seven casted bars were homogenized at 1200°C for a period of 2 hours. Then, they were immediately hot rolled after homogenization so that the out rolling temperature was kept in the range of 1000-1200° C. The specimens were then solution annealed at 820°C for hour and finally they were aged for a period of 3 hours at 500°C. The samples were subjected to tensile, impact and hardness tests in order to relate the variation in volume percent of inclusions due to different amount of Ti, to mechanical properties. The results showed that by increasing the amount of Ti a serious decline in toughness properties of the alloy due to increase in inclusion population occurred. So this research provides a very useful information about the relation between volume fraction of inclusions and mechanical properties of a C300 high strength steel.