Showing 3 results for Amiri
M. M. Kashani Motlagh, A. A. Youzbashi, Z. Amiri Rigi,
Volume 8, Issue 4 (december 2011)
Abstract
A natural bentonite obtained from Khorasan, Iran, was submitted to acid activation with sulphuric acid. Sample aliquots (5gr)
were leached with 100 ml H2SO4 solutions of various concentrations (2–7N) at 80±2 oC for 2 hours. X–ray diffraction, chemical analysis, infrared spectroscopy and specific surface area measurements were performed in order to evaluate important structural modifications occurring as a result of acid attack. Octahedral sheet was affected by acid activation resulting into the dissolution of cations (Mg2+, Fe2+, Al3+) and consequent decomposition of montmorillonite structure. Bentonite samples were then tested in order to verify their capacity to bleach colza–soybean oil, and their performances were compared to that of a commercial bleaching clay. The bleaching ability of the natural clay was poor when compared with that of the industrial adsorbent. Acid activation of the bentonite sample with 7N sulphuric acid yielded an adsorbent material which was highly efficient in the bleaching of the oil functioned better than the commercial clay product under the same conditions.
M. Bahamirian, Sh. Khameneh Asl,
Volume 10, Issue 3 (September 2013)
Abstract
In the present study NiCrAlY bond coating layer was produced by electroplating against common atmospheric plasma spraying (APS). Both types of the bond coats were applied on IN738LC base metal then, the YSZ (ZrO2-8% Y2O3) thermal barrier top layer was coated by atmospheric plasma spray technique. Hot corrosion is one of the main destructive factors in thermal barrier coatings (TBCs) which come as a result of molten salt effect on the coating–gas interface. In this investigation the hot corrosion behavior of coatings was tested in the furnace which was contain Na2SO4-55% V2O5 and mixed salts environment at 900°C up to 15 hr. dwell time. Optical microscopy, scanning electron microscopy (SEM / EDS) and X-ray diffraction analysis (XRD) was used to determine the crystallographic structure and phase transformation of the coatings before and after the hot corrosion tests. The transformation of tetragonal Zirconia to monoclinic ZrO2 and formation of YVO4 crystals as hot corrosion products caused the degradation of mentioned TBCs. The results showed NiCrAlY coated by economical electroplating method a viable alternative for common thermals sprayed bond coats in hot corrosive environments with same corrosion behavior
S. Kord, M. H. Siadati, M. Alipour, H. Amiri, P.g. Koppad, A. C. Gowda,
Volume 15, Issue 4 (December 2018)
Abstract
The effects of rare earth element, erbium (Er) additions on the microstructure and mechanical properties of Al-15Zn-2.5Mg-2.5Cu alloy have been investigated. This new high strength alloy with erbium additions (0.5, 1.0, 1.5 and 2.0 wt%) was synthesized by liquid metallurgy route followed by hot extrusion. Microstructural characterization was performed using scanning electron microscope and electron probe microanalysis. Significant amount of grain refinement was observed with erbium addition in the hot extruded and heat treated alloy. Tensile test was performed to investigate the effect rare earth on mechanical behavior of alloy in as cast and hot extruded condition before and after T6 heat treatment. The combined effect of erbium addition, hot extrusion and heat treatment significantly enhanced the tensile strength of alloy (602 MPa) when compared to the as cast alloy without erbium addition (225 MPa). The strengthening of the alloy was attributed to grain refinement caused by erbium along with hot extrusion and formation of precipitates after T6 heat treatment. Fractograhic investigations revealed that the hot extruded alloy with erbium addition after heat treatment showed uniformly distributed deep dimples exhibiting ductile behavior.