FATEMI NAYERI S.H.R., ABOUTALEBI M.R., VAHDATI KHAKI J.. THE EFFECT OF MILLING CONDITIONS ON THE MECHANICAL ALLOYING AND COMBUSTION SYNTHESIS OF TIO2-AI-C POWDER MIXTURE

. IJMSE 2006; 3 (1) :9-15
URL: http://ijmse.iust.ac.ir/article-1-82-en.html
Abstract:   (27243 Views)
A mixture of Tio2+Al+C powders was mechanically activated using a planetary ball mill under different milling conditions wherein the milled powders were further subjected to combustion synthesis to produce TiC+Al2O3 composite. The mechanically alloyed powders were characterized by X-Ray diffraction analysis and TEM investigations. XRD analysis of milled powder mixture showed no significant reaction between TiO2, Al and C while a significant amorphization of powder mixtures was observed. TEM analysis indicated the formation of a composite structure of powder particles after milling. The subsequent thermal treatment of the milled powder mix showed that the milling of initial powder mixture under dry environment using mixed large and small balls had a great effect on reaction efficiency and yielded to the highest TiC + Al2O3 ratio in the synthesized products.
     
Type of Study: Research Paper | Subject: Ceramics

Add your comments about this article : Your username or Email:
CAPTCHA

Rights and permissions
Creative Commons License This work is licensed under a Creative Commons Attribution-NonCommercial 4.0 International License.

© 2022 All Rights Reserved | Iranian Journal of Materials Science and Engineering

Designed & Developed by : Yektaweb