Yazdani A, Zakeri R. FEASIBILITY OF PRODUCING NANO STRUCTURED METALLIC AND NON-METALLIC COATINGS ON Al SUBSTRATE USING MECHANICAL COATING ROUTE. IJMSE 2015; 12 (2) :26-33
URL: http://ijmse.iust.ac.ir/article-1-800-en.html
URL: http://ijmse.iust.ac.ir/article-1-800-en.html
Abstract: (20982 Views)
In this paper, the possibility of mechanical coating of aluminum with either Ni or SiC using planetary ball
mill was studied. The Al substrate was fixed inside of the vial lid of a planetary ball mill filled with milling balls and
starting powder. The phase analysis and crystallite size measurement of the coatings were carried out using X-ray
diffraction (XRD) method. Scanning electron microscope (SEM) was employed to study the coating/substrate interface
and coating thickness. Hardness and wear resistance of coatings were also measured. The results indicated that all
coatings have relatively uniform thickness. SiC coating shows poor compaction and adhesion to the Al, while nanostructured Ni coating is well-bonded to the substrate. Moreover, Ni coating showed higher hardness and wear
resistance compared to SiC coating. It was found that the balls collision will result in the grain refinement of the
coating as well as Al substrate. Mechanically deposited Ni coating shows higher hardness value compared to those
obtained by conventional methods. This has been related to the induced grain refinement phenomenon.