Lekmine F, Ben Temam H, Temam E. Characterization of Nanocrystalline NiP Alloy Coatings Electrodeposited at Various Current Densities. IJMSE 2021; 18 (3) :1-7
URL: http://ijmse.iust.ac.ir/article-1-2237-en.html
Characterization of Nanocrystalline NiP Alloy Coatings Electrodeposited at Various Current Densities
Farid Lekmine , Hachemi Ben Temam , Elhachmi Temam
Abstract:   (9342 Views)
Nickel phosphorus alloy coatings were prepared by electrodeposition route from sulfate electrolyte bath at various current densities. SEM studies reveal spherical grains covered the entire surface with uniform distribution. EDX results showed a linear increase of P content in the developed deposits with current density and therefore, enhancing the grains size and drop of the hardness values. XRD studies reveal monocrystalline orthorhombic alloys at a low amount of phosphorus (10.88 wt. %). Corrosion tests show that 1 A.dm-2 is the best applied current density giving the nobler Ecorr (-171.4 mV) and the lower icorr (4.64 µA/cm2).
Keywords: Ni–P alloy coatings, Crystal structure, P content, Hardness, Electrochemical properties.
Full-Text [PDF 1594 kb]   (6275 Downloads)    
Type of Study: Research Paper | Subject: Ceramics
Add your comments about this article : Your username or Email:
CAPTCHA
Send email to the article author

Rights and permissions
Creative Commons License This work is licensed under a Creative Commons Attribution-NonCommercial 4.0 International License.

© 2022 All Rights Reserved | Iranian Journal of Materials Science and Engineering

Designed & Developed by : Yektaweb