Borhani G H, Bakhshi S R, Soltani S. The Effect of Temperature on the Purity of Nano-Scale Tantalum Powder Produced from Its Scrap by Reaction with Magnesium and Calcium. IJMSE 2021; 18 (2) :1-7
URL: http://ijmse.iust.ac.ir/article-1-2006-en.html
The Effect of Temperature on the Purity of Nano-Scale Tantalum Powder Produced from Its Scrap by Reaction with Magnesium and Calcium
Gholam Hussein Borhani , Saeed Reza Bakhshi , Sadegh Soltani
Abstract:   (10794 Views)
In this study, Ta powder was produced from Ta scarp via chemical processes using Mg and Ca powders. At first, Tantalum scraps were converted to Tantalum oxide (Ta2O5) at 1100˚C in an oxygen atmosphere. Tantalum oxide was reduced to Tantalum powder with Mg in a vacuum environment at 950 to 1200˚C for 3 hours. The obtained Ta powders further were reacted with Ca at 950˚C for 5 hours in a vacuum atmosphere. The powders were analyzed through X-ray diffraction patterns (XRD), scanning electron microscopy (SEM), as well as oxygen measurement. The results show that the average particles size of the produced Ta powders is about 58 nm with oxygen contents of 250 ppm.
Keywords: tantalum, refractory metal, magnesium, recovery process, magnesiothermic reduction
Full-Text [PDF 2180 kb]   (3766 Downloads)    
Type of Study: Research Paper | Subject: Ceramics
Add your comments about this article : Your username or Email:
CAPTCHA
Send email to the article author

Rights and permissions
Creative Commons License This work is licensed under a Creative Commons Attribution-NonCommercial 4.0 International License.

© 2022 All Rights Reserved | Iranian Journal of Materials Science and Engineering

Designed & Developed by : Yektaweb