SAGHAFIAN LARIJANI H., RAINFORTH W. M.. PLASTIC DEFORMATION BEHAVIOUR AT THE WORN SURFACE OF NOVEL CAST AL-ALLOY-TICP COMPOSITE. IJMSE 2004; 1 (3) :9-15
URL: http://ijmse.iust.ac.ir/article-1-15-en.html
Abstract:   (41157 Views)
An AI-7wt%Si-5vol%TiCp was worn against a cast iron disc in a tri-pin-on-disc machine, under dry sliding conditions at the sliding speed of 0.24 m/s and applied loads of 6, 20 and 40 N/pin. Stress-strain (σ-ε) curves were constructed by measuring the microhardness and the equivalent strain gradients in near surface regions on the cross-sectional surface prepared parallel to sliding direction.It was shown that, both the magnitude of plastic strains and the depth of plastic deformed zones increased with the applied load. The material exhibited considerable work softening in addition to work hardening at the highest applied load. The softened layer placed just beneath the mechanical mixed layer (MML), was mostly covered with the fine fractured eutectic Si and TiC fragments most of which were associated with microcracks at Al/Si and Al/TiC interfaces. The results were discussed in terms of some of the current work hardening models.
     
Type of Study: Research Paper | Subject: Ceramics

Add your comments about this article : Your username or Email:
CAPTCHA

Rights and permissions
Creative Commons License This work is licensed under a Creative Commons Attribution-NonCommercial 4.0 International License.

© 2022 All Rights Reserved | Iranian Journal of Materials Science and Engineering

Designed & Developed by : Yektaweb