L16 Orthogonal Design Synthesis of NASICON-type Li1.4Al0.4Ti1.6(PO4)3 Solid Electrolyte by Pechini Method for Process Optimization

Ghaani, M. R.; Marashi, P.

doi:10.22068/ijmse.15.3.60

Volume 15, Issue 3 (September 2018) IJMSE 2018, 15(3): 60-71 | Back to browse issues page

‎ 10.22068/ijmse.15.3.60

Mendeley

Zotero

RefWorks

Ghaani M R, Marashi P. L16 Orthogonal Design Synthesis of NASICON-type Li1.4Al0.4Ti1.6(PO4)3 Solid Electrolyte by Pechini Method for Process Optimization. IJMSE 2018; 15 (3) :60-71
URL: http://ijmse.iust.ac.ir/article-1-1088-en.html

L16 Orthogonal Design Synthesis of NASICON-type Li1.4Al0.4Ti1.6(PO4)3 Solid Electrolyte by Pechini Method for Process Optimization

M. R. Ghaani

, P. Marashi

Abstract: (22429 Views)

Na super ionic conductive (NASICON) materials are ceramics with three-dimensional scaffolds. In this study, Li_1.4Al_0.4Ti_1.6(PO₄)₃ with NASICON structure was synthesized by Pechini method. As a result, a sample having a total conduction of 1.18×10^-3 S cm^-1 was attained. In addition, various parameters were studied to obtain high value of conductivity, by optimizing the process. The optimization was made using L16 Taguchi based orthogonal array, followed by ANOM, ANOVA and stepwise regression. As a result, the optimum synthesis parameters can be obtained, while pH of the solution was adjusted to 7. The ratio between the concentration of citric acid to metal ions and ethylene glycol concentration stuck to 1 and 2.5, respectively. The best heat treatment can be carried out with a combination of pyrolysis at 600 ºC and sintering at 1000 ºC.

Keywords: NASICON, Pechini, Ionic conductivity, ANOM, Stepwise regression, Electrochemical impedance spectroscopy, LATP, Peroxotitanium.